| 牌号简介 About |
|---|
| Riblene® FC 39 F是一种高分子量低密度聚乙烯（LDPE），适用于吹塑薄膜挤出。Riblene® FC 39 F的特点是具有较高的熔融强度，在挤压过程中具有良好的气泡稳定性。由Riblene® FC 39 F制造的薄膜容易热收缩，具有高硬度、良好的机械和光学性能。主要应用Riblene® FC 39 F推荐用于生产中等硬度的收缩膜，具有良好的清晰度和光泽。 Riblene FC 39 F is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FC 39 F is characterised by a high melt strength leading to a good bubble stability during extrusion. Films manufactured by Riblene FC 39 F are easily heat shrinkable and characterised by high rigidity, good mechanical and optical properties. Main Application Riblene FC 39 F is recommended for the production of medium rigidity shrink film characterized by good clarity and gloss. |
产品描述 Product Description
用途：薄膜;收缩性薄膜;
加工条件：吹塑薄膜
性能特点： 熔体强度好; 热收缩性好; 机械强度好; 透光性好; 高分子量; 食品接触; 光学性能; 表面光泽度好; 低密度; Good Rigidity,Good Clarity,Good surface appearance,Optical performance,Food contact compliance,High molecular weight,Good melt strength,Low density,Good thermal contraction
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.924 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
0.25 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 friction coefficient |
|||
|
与自身 - 动态，吹塑薄膜 Self dynamic, blow molded film |
> 0.50 | ISO 8295 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
70 | µm | |
|
薄膜厚度 film thickness |
40-150 µm | ||
|
拉伸模量 Tensile modulus |
ISO 527-3 | ||
|
1% 正割，MD，70 µm，吹塑薄膜 1% secant, MD, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
|
1% 正割，TD，70 µm，吹塑薄膜 1% secant, TD, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，70 µm，吹塑薄膜 MD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，屈服，70 µm，吹塑薄膜 TD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
|
MD，断裂，70 µm，吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，70 µm，吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，70 µm，吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
|
TD，断裂，70 µm，吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact 2 |
|||
|
70 µm，吹塑薄膜 70 µ m, blow molded film 2 |
g | ISO 7765-1 | |
|
撕裂强度 tear strength 3 |
ISO 6383-2 | ||
|
MD，70 µm MD，70 µm |
kN/m | ISO 6383-2 | |
|
TD，70 µm TD，70 µm |
kN/m | ISO 6383-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，70 µm，吹塑薄膜 45 °, 70 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
70.0 µm，吹塑薄膜 70.0 µ m, blow molded film |
% | ISO 14782 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
| 3 Blown Film |
|
【新闻资讯】查看全部 
医用高分子植入材料市场发展前景可期
2021-03-20 搜料网资讯： 美国医疗行业咨询公司N-tech Research发表报告称，到2021年，医用高分子植入材料的全球销售额可达17亿美元。该公司还预测整个医用假体行业很快将向可降解聚合物方面发展 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付