| 牌号简介 About |
|---|
| LEXAN 943是一种中等粘度，阻燃PC，紫外线稳定等级，特别适用于电气应用。 LEXAN 943 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This brominated flame retardant PC has a UL-94 V0 rating and is UV stabilized, providing additional weathering capability. LEXAN 943 resin is available in limited opaque color options and is a general-purpose resin ideal for a wide variety of applications. As a non-chlorinated, non-brominated flame retardant solution, LEXAN 945U resin could be considered an alternative. |
产品描述 Product Description
性能特点： 防火阻燃等级V-0; 阻燃; 耐候抗UV; Weather resistance is good,Flame Characteristics,V-0
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ISO 1183 |
|
熔体体积流率（MVR）（300℃/1.2 kg） Melt Volume Flow Rate (MVR) (300 ℃/1.2 kg) |
9.5 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.50 to 0.70 | % | 内部方法 |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
0.35 | % | ISO 62 |
|
平衡，100℃ Equilibrium, 100 ℃ |
0.15 | % | ISO 62 |
|
球压硬度 Ball hardness |
|||
|
H358/30 H358/30 |
MPa | ISO 2039-1 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ISO 527-2/50 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
泰伯耐磨性 Taber abraser |
|||
|
1000 周期，1000 g，CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | 内部方法 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
|
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
-30℃ -30℃ |
ISO 179/1eU | ||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
|||
|
-30℃ -30℃ |
ISO 180/1U | ||
|
23℃ 23℃ |
ISO 180/1U | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火，100 mm跨距 1.8 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Be | |
|
0.45 MPa，未退火，100 mm跨距 0.45 MPa, unannealed, 100 mm span |
℃ | ISO 75-2/Be | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
球压测试 Ball pressure test |
|||
|
125℃ 125℃ |
IEC 60695-10-2 | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：23~80℃ MD：23~80℃ |
1/℃ | ISO 11359-2 | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ISO 8302 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
|||
|
3.2 mm，在空气中 3.2 mm in air |
kV/mm | IEC 60243-1 | |
|
介电常数 Dielectric constant |
|||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
60 Hz 60 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
IEC 60250 | ||
|
60 Hz 60 Hz |
IEC 60250 | ||
|
1 MHz 1 MHz |
IEC 60250 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
灼热丝可燃性指数 Glowing wire flammability index |
|||
|
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
|
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Thickness: 2 to 3 mm |
| 3 0.20 in/min |
| 4 0.12 in/min |
| 5 压 力1 (10N) |
|
【新闻资讯】查看全部
如何更好运用TPU为汽车配件保驾护航？
2017-03-13 亨斯迈(Huntsman)的两款热塑性聚氨酯(TPU)产品正在推动汽车配件的运输方式发生变革，为代工生产商(OEM)和汽车制造商节省大量时间和金钱。 PolyFlex Products(以下简称“PFP”)是一家位于美国生产专业衬垫的制造商，目前正采用亨斯迈IROGRAN和AVALON品牌下的两款耐磨TPU产品大幅改善其定制托盘、集装箱、巢箱和货架的性能并延长使用寿命。 改用TPU产品之后，确保PFP公司的衬垫产品经久耐用，使用寿命长达5年，同时还大幅降低非 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |