牌号简介 About |
---|
HOSTACOM TRC 352N高熔体流动性、高弯曲模量、矿物填充热塑性弹性烯烃(TEO)树脂具有优异的冲击/刚度平衡、良好的流动性和优异的耐刮性。它在高温下具有优异的耐开花性。它主要是为汽车内部应用而设计的。 Hostacom TRC 352N high melt flow, high flexural modulus, mineral-filled thermoplastic elastomeric olefin (TEO) resin has excellent impact/stiffness balance, good flowability properties, and excellent scratch resistance. It has an outstanding blooming resistance at elevated temperatures. It was designed primarily for interior automotive applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
18 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
20.0 | MPa | ISO 527-2/50 |
弯曲模量 Bending modulus 2 |
|||
23℃ 23℃ 2 |
1850 | MPa | ISO 178 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
4.5 | kJ/m² | ISO 179/1eA |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179/1eU |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
三棵树品牌代言人谷爱凌勇夺本届冬奥会中国代表团雪上首金!
2022-02-13 2月8日上午,在北京冬奥会自由式滑雪女子大跳台决赛中, 三棵树 品牌代言人,中国选手谷爱凌凭借第三跳上的出色发挥,拿到全场最高分,最终以188.25的总分获得冠军。这是中国女选 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |