牌号简介 About |
---|
KetaSpire KT -820是低流动级未增强聚醚醚酮(PEEK),呈润滑颗粒状。KetaSpire PEEK按照行业最高标准加工,以兼具不同的性能为特征,包括优异的耐磨损性、一流的抗疲劳性、易于熔融加工、高纯度、优异的耐有机物、酸和碱等化学物质的性能。 这些特性使得它非常适合医疗保健、交通运输、电子、化学处理和其它工业用途。KetaSpireKT -820可以很容易地使用常规注塑成型和挤出工艺进行加工。有本色粗粉末牌号KetaSpire KT- 820P供配混。 粒状KT- 820微量喷洒了润滑剂硬脂酸钙( 0.01 % ),方便颗粒在塑化螺杆中的输送。有类似于非润滑本色低流量牌号KetaSpire KT -820 NL可供 。 黑色:KT-820 BK 95 KetaSpire® KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing, and other industrial uses. KetaSpire® KT-820 can be easily processed using typical injection molding and extrusion processes. This resin is also available as KetaSpire® KT-820P in a natural-color coarse powder form for compounding. Pellets of KT-820 are supplied lightly dusted with the lubricant calcium stearate (0.01% level) to aid with pellet conveyance in plastication screws. The equivalent non-lubricated natural color grade of low flow KetaSpire® is available as KT-820 NL. Black: KT-820 BK 95 Natural: KT-820 NT |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-- -- |
91 | J/m | ASTM D256 |
-- -- |
9.2 | kJ/m² | ISO 180 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
无断裂 | ASTM D4812 , ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 9 |
|||
1.8 MPa,退火,3.2 mm 1.8 MPa, annealed, 3.2 mm 9 |
157 | ℃ | ASTM D648 |
玻璃化转变温度 Glass transition temperature |
150 | ℃ | ASTM D3418 |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-50~50℃ MD:-50~50℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
DSC | ||
50℃ 50℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
2.5 mm 2.5 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 kHz 1 kHz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,1 秒 Shore D, 1 second |
ASTM D2240 | ||
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- 7 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/1A/50 | |
-- -- 7 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield 7 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/1A/50 | |
断裂 fracture 8 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 , ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
ASTM E132 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
熔体质量流动速率 Melt Flow Rate |
|||
400℃,2.16kg 400℃,2.16kg |
g/10min | ASTM D1238 | |
收缩率 Shrinkage rate 6 |
ASTM D955 | ||
MD MD |
% | ASTM D955 | |
TD TD |
% | ASTM D955 | |
吸水率 Water absorption rate |
|||
24hr 24hr |
% | ASTM D570 | |
熔体表观粘度 Apparent viscosity of melt |
|||
400℃,1000 sec^-1 400℃,1000 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 Passes 60s VB flame, smoke & toxicity requirements. |
2 供应塑料粒子里加入润滑剂硬脂酸钙(0.01 % )的牌号,对于非润滑、本色牌号,订购KT- 820 NL 。 |
3 一般属性:这些不能被视为规格。 |
4 0.125"x0.5"x5" bar |
5 2.0 in/min |
6 0.20 in/min |
7 200°C,2小时 |
【新闻资讯】查看全部
万华化学荣登A股公司ESG百强榜
2021-11-12 搜料网资讯: 近日,由证券时报编制的《A股公司ESG百强榜》发布。凭借在环境(E)、社会(S)、公司治理(G)三维得分上的突出成绩,万华化学荣登榜单。 ESG是一种关注企业环境、社会、公 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |