| 牌号简介 About |
|---|
| IROGRAN® A 70 E 4675是一种不含柔软剂的热塑性专用聚酯聚氨酯，用于注塑成型。该产品的附加特性是循环时间短，尺寸稳定性高。性能特点：易于拆模、高拆模稳定性、短周期时间软化剂、自由高弹性应用于休闲鞋底、电缆套管、插头、缓冲器的生产。 IROGRAN A 70 E 4675 is a softener free thermoplastic special-polyester-polyurethane for injection moulding applications. Additional characteristics of the product are very short cycle times and high dimensional stability. PERFORMANCE FEATURES Easy demolding High demolding stability Short cycle times Softener-free High elasticity APPLICATIONS For the production of casual shoe soles, cable bushings, plugs, buffers. |
产品描述 Product Description
用途：鞋类;衬套;插头;
加工条件：注射成型 Injection Molding
性能特点： 尺寸稳定性好; 含脱模剂; 成型周期快; 柔软性好; 弯曲性能好; Good Dimensional Stability,High elastic,Quick molding cycle,Good stripping performance,Soft
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density 2 |
1.15 | g/cm³ | |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
190℃，21.6 kg 190℃，21.6 kg |
30.0 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate 2 |
2.5 | % | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ISO 868 | ||
|
邵氏 A，注塑成型 Shaw A, injection molding |
75 | ISO 868 | |
|
邵氏 D，注塑成型 Shaw's D, injection molding |
25 | ISO 868 | |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 A，注塑成型 Shaw A, injection molding |
ASTM D2240 | ||
|
邵氏 D，注塑成型 Shaw's D, injection molding |
ASTM D2240 | ||
|
Abrasion Abrasion 2 |
mm³ | ISO 4649 | |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength 2 |
|||
|
断裂 fracture 2 |
MPa | DIN 53504 | |
|
断裂 fracture 2 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 2 |
MPa | ASTM D412 | |
|
300% 应变 300% strain 2 |
MPa | DIN 53504 | |
|
100% 应变 100% strain 2 |
MPa | ASTM D412 | |
|
100% 应变 100% strain 2 |
MPa | DIN 53504 | |
|
拉伸应变 Tensile strain 2 |
|||
|
断裂 fracture 2 |
% | ASTM D412 | |
|
断裂 fracture 2 |
% | DIN 53504 | |
|
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
|
撕裂强度 tear strength 2 |
kN/m | ISO 34-1 | |
|
压缩形变 Compression deformation 2 |
ASTM D395 | ||
|
23℃，24 hr 23℃，24 hr |
% | ASTM D395 | |
|
70℃，24 hr 70℃，24 hr |
% | ASTM D395 | |
|
压缩形变 Compression deformation 2 |
ISO 815 | ||
|
23℃，24 hr 23℃，24 hr |
% | ISO 815 | |
|
70℃，24 hr 70℃，24 hr |
% | ISO 815 | |
|
巴肖氏弹性 Basho's elasticity |
% | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
熔融温度 Melting temperature |
℃ | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 Injection Molded |
|
【新闻资讯】查看全部 
博创Bi订单暴涨40倍 Bi设计团队获奖75万
2021-03-01 搜料网资讯： 博创基于近二十年专注于注塑装备研发生产的雄厚根基，经过多年深耕细作研发出Bi智能注塑机，于2019年开始各机型小批量投放市场，2020年全线上市，一举获得亿元订单， |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付