牌号简介 About |
---|
SABIC® HDPE BM6246LS是一种高密度聚乙烯吹塑级高刚性,韧性好,加工性好。这些性能提供了瓶子在较低的重量和非常好的顶部负荷强度。典型应用。SABIC® HDPE BM6246LS通常用于吹塑瓶包装感官敏感产品,例如牛奶、果汁和其他乳制品。不建议用于包装环保材料,如肥皂、清洁剂、洗发水等。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® HDPE BM6246LS is a high density polyethylene blow moulding grade for high rigidity, good toughness and good processability. These properties offer bottles to be made at lower weight with very good top load strength. Typical applications. SABIC® HDPE BM6246LS is typically used for blow moulding bottles for packaging organoleptically sensitive products, e.g. milk, fruit juice and other dairy products. It is not recommended for packaging environmentally active materials such as soaps, detergents, shampoos, etc. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.961 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | |
190℃,21.6kg 190℃,21.6kg |
46 | g/10min | |
190℃,5.0kg 190℃,5.0kg |
2.5 | g/10min | |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
10%非离子洗涤剂,模压成型,F50 10% non-ionic detergent, molded, F50 |
15.0 | hr | ASTM D1693B |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃,模压成型 -30 ℃, molded |
kJ/m² | ||
23℃,模压成型 23 ℃, molded |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 11357-3 | |
Enthalpy Change Enthalpy Change |
J/g | ISO 11357-3 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吹塑成型料筒温度 Blow molding barrel temperature |
℃ | ||
Blow Molding Melt Temperature Blow Molding Melt Temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 527-2/1BA/50 | |
拉伸强度 tensile strength |
ISO 527-2/1BA/50 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
% | ISO 527-2/1BA/50 | |
弯曲模量 Bending modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
活动模拟技术在注塑成型设计中的使用
2016-01-25 塑料注射成型在塑料制品中占有很大比重,在传统的注射模设计及加工方法中,有些设计参数只能依靠有限的资料和经验确定,但塑料注射成型过程十分复杂,单纯依靠传统的经验设计和制造方法已很难满足生产质量要求。 注射模CAD/CAE/CAM的重点在于注射产品的造型、模具设计、绘图和数控加工数据的生成,而CAE包含的工程功能则更广泛。CAE将工程设计、试验、分析、文件生成以及制造贯穿于产品研制过程的每个环节,以指导和预测产品在构思和设计阶段的行为。CAD/CAE/CAM的集成化从根本上改变 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |