AOC的Vipel K010-TB系列是一种促进双酚A,环氧基乙烯基酯树脂溶于苯乙烯和甲基丙烯酸甲酯。通过在每100份树脂中加入至少60份三水合物氧化铝,可获得阻燃和防烟性能。VIPEL K010-TB系列最适合用于手工铺层、喷涂和纤维缠绕工艺,其中突出的机械性能和优异的耐化学品和耐热性是必需的。福利广泛的制定能力允许在许多过程中使用,并优化成本/性能。独特的组成产生了一个坚韧和多用途的树脂,具有优异的裂缝和耐开裂性的模件。VIPEL K010-TB系列适用于承受特别高静态或动态载荷的模具。乙烯基酯树脂具有优异的耐热性。VIPEL K010-TB系列树脂对多种化学环境有很高的抵抗力。 AOC's Vipel K010-TB series are promoted bisphenol A, epoxy-based vinyl ester resins dissolved in styrene and methyl methacrylate. Flame and smoke resistance is obtained by incorporating at least 60 parts of alumina trihydrate per 100 parts of resin. Vipel K010-TB series are ideally suited for use in hand lay-up, spray-up and filament winding processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. BENEFITS Wide formulating capabilities allow for use in many processes and for optimization of cost/performance. Unique composition produces a tough and versatile resin with excellent crack and craze resistance in molded parts. Vipel K010-TB series is suitable for moldings that are subjected to particularly high static or dynamic loads. Vinyl ester resins have excellent resistance to sustained heat. Vipel K010-TB series resins are highly resistant to several chemical environments. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3600 | MPa | ASTM D638 |
拉伸强度 tensile strength |
89.6 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
4.0 | % | ASTM D638 |
弯曲模量 Bending modulus |
3700 | MPa | ASTM D790 |
弯曲强度 bending strength |
155 | MPa | ASTM D790 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
min | ||
HAP Content HAP Content |
% | ||
放热峰值 exothermic peak |
℃ | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 LV Brookfield LV |
Pa·s | ||
胶凝时间 Gelation time |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
北京最严“限塑令”来了!业内建议源头减量和循环利用并重
2020-12-19 搜料网资讯: 全球每年塑料总消费量4亿吨,中国消费超6000万吨,最终被有效回收的只有10%。每年超10万只海洋动物,因被塑料袋缠住或误食塑料袋而死亡。塑料购物袋在为消费者提供便 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |