牌号简介 About |
---|
成型参数:16小时干燥温度165°F,2区机后温度510-540°F,前温度500-530°F。 Molding Parameters: The dry temperature at 16 hours is 165°F. For 2-zone machines, the rear temperature is 510-540°F, and the front temperature is 500-530°F. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.55 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.12 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.33 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
64 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃,3.2 mm 23℃,3.2 mm |
270 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
原油最大卖家沙特阿美售价上涨 看好市场持续火热
2022-02-08 油价已经触及逾七年高位,但沙特阿美最新的定价显示油价不会很快下跌。 沙特阿美周末发布了月度官方原油售价。对于从亚洲到美洲的买家而言,3月每桶原油的价格相对于地区基准 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |