Pocan B 3216 HR 000000 PBT,16%玻璃纤维,注塑成型,提高冲击强度,水解稳定 POCAN® B3216HR 000000 PBT, 16 % glass fibers, injection molding, improved impact strength, hydrolysis stabilized POCAN® B3216HR 000000 PBT, 16 % glass fibers, injection molding, improved impact strength, hydrolysis stabilized POCAN® B3216HR 000000 PBT, 16 % glass fibers, injection molding, improved impact strength, hydrolysis stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.40 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,2.16 kg 260℃,2.16 kg |
24.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:260℃,2.0 mm TD:260℃,2.0 mm |
1.0 | % | ISO 294-4 |
TD:120℃,2.0 mm,2 hrs TD:120℃,2.0 mm,2 hrs |
0.10 | % | ISO 294-4 |
MD:260℃,2.0 mm MD:260℃,2.0 mm |
% | ISO 294-4 | |
MD:120℃,2.0 mm,2 hrs MD:120℃,2.0 mm,2 hrs |
% | ISO 294-4 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178-A | |
弯曲强度 bending strength |
|||
3.50% 应变 3.50% strain |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 7792 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2; MT 80°C; 600 Bar |
3 60x60x2mm, 80°C MT, 600 bar |
4 60x60x2 |
5 60x60x2mm |
6 0.079 in/min |
7 Pull Rate: 2 mm/min; 50% RH |
8 2 mm/min |
9 10°C/min |
【新闻资讯】查看全部
劳动力成本仅中国的五分之一!东南亚取代中国成多数国际服装代工地
2022-01-18 搜料网资讯: 2021年中国服装出口创2015年来同期新高,但安永咨询服务合伙人周亮认为这一成绩并不牢靠。 据中国海关统计,2021年1-11月,我国服装出口达1592.7亿美元,同比增长25.4%。此 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |