公司信息及水印
牌号简介 About |
---|
O19010是一种基于辛烯共聚单体的线性低密度聚乙烯(LLDPE),具有最佳水平的抗氧化剂、防堵剂、防滑添加剂和聚合物加工助剂。该等级设计用于制造超高负荷应用和液体包装用的吹塑薄膜,在这种情况下,需要通过污染、韧性、冲击强度和抗撕裂性实现良好的密封。 O19010 is an octene comonomer based Linear Low Density Polyethylene (LLDPE), with optimum levels of antioxidant, antiblocking agent, slip additive and polymer processing aid. The grade is designed to make blown film for ehavy duty applications and liquid packaging, where excellent seal through contamination, toughness, impact strength and tear resistance are desired. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
0.12 | ASTM D1894 | |
与自身 - 静态,吹塑薄膜 Compared to itself - static, blow molded film |
0.20 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,40 µm,吹塑薄膜 MD, yield, 40 µ m, blow molded film |
12.5 | MPa | ASTM D882 |
TD,屈服,40 µm,吹塑薄膜 TD, yield, 40 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
g | ASTM D1922 | |
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,40.0 µm,吹塑薄膜 60 °, 40.0 µ m, blow molded film |
ASTM D523 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
宁夏启动碳达峰碳中和与可持续发展战略研究项目
2021-07-08 搜料网资讯: 7月8日,宁夏碳达峰碳中和与可持续发展战略研究项目启动会在银川召开。项目依托中国矿业大学,联合安徽理工大学、江苏省碳中和联合研究中心、宁夏回族自治区生态 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |