公司信息及水印
牌号简介 About |
---|
DOWLEX™ GM 8480G聚乙烯树脂适用于铸造拉伸薄膜应用,具有良好的延展性,同时保持良好的穿刺和负载保持力。主要特点:延展性好,穿刺和负重保持性好。 DOWLEX™ GM 8480G Polyethylene Resin is suitable for cast stretch film applications with superior extensibility while maintaining good puncture and load retention. Main Characteristics: Superior extensibility Good puncture and load retention |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness 2 |
|||
测试 test 2 |
20 | µm | |
膜耐刺穿性 Membrane puncture resistance |
22.9 | J/cm³ | 内部方法 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
9.97 | MPa | ASTM D882 |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ASTM D1922 | |
TD TD |
g | ASTM D1922 | |
Film Stretch Performace(On Pallet Puncture) Film Stretch Performace(On Pallet Puncture) |
N | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
最大伸长率 Maximum elongation |
% | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 |
备注 |
---|
2 Cast |
【新闻资讯】查看全部
【 助减排率提高70%】针对汽车的新型生物基塑料
2020-10-14 搜料网资讯: 由于绿色材料能够确保移动出行的可持续性,因此汽车行业正不断地致力于使汽车生产符合可持续发展的原则。而开发合适的材料在这一过程中起着决定性的作用。 凭借生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |