牌号简介 About |
---|
HEPLA®H9016GF T H聚邻苯二甲酰胺(PPA)是一种增韧、热稳定的16%玻璃纤维增强树脂,是一种经济有效的解决方案,适用于要求刚度、良好尺寸稳定性、耐化学性和延展性的应用。该树脂具有较高的热变形温度和较高的弯曲模量。轴承保持架/保持架、外壳、化学加工设备部件、电机框架、运动设备、草坪和花园设备以及需要压装或卡装组件的部件。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.28 | 3 | ISO 1183/A |
收缩率 Shrinkage rate |
|||
MD MD |
0.6 | % | ASTM D955 |
TD TD |
0.6 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24 hr 24 hr |
0.2 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
|
6480 | MPa | ASTM D638 |
23℃ 23℃ |
MPa | ISO 527-2 | |
100℃ 100℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
|
MPa | ASTM D638 | |
Break,23℃ Break,23℃ |
MPa | ISO 527-2 | |
Break,100℃ Break,100℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
Break,23℃ Break,23℃ |
% | ISO 527-2 | |
Break,100℃ Break,100℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
|
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
|
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
100℃ 100℃ |
MPa | ISO 178 | |
抗压强度 compressive strength |
MPa | ASTM D695 | |
Shear Strength Shear Strength |
MPa | ASTM D732 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180/1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
飞镖冲击强度 Dart impact strength |
|||
Energy at Maxumum Load 1 Energy at Maxumum Load 1 |
J | ASTM D3763 | |
Energy at Maxumum Load 2 Energy at Maxumum Load 2 |
J | ||
Total Energy Total Energy |
J | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa, Annealed 0.45 MPa, Annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa, Annealed 1.8 MPa, Annealed |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418,ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
Flow : 0 to 100℃ Flow : 0 to 100℃ |
cm/cm/℃ | ASTM E831 | |
Flow : 100 to 200℃ Flow : 100 to 200℃ |
cm/cm/℃ | ASTM E831 | |
Transverse : 0 to 100℃ Transverse : 0 to 100℃ |
cm/cm/℃ | ASTM E831 | |
Transverse : 100 to 200℃ Transverse : 100 to 200℃ |
cm/cm/℃ | ASTM E831 |
备注 |
---|
1 Maximum Load: 200 lb (890 N) |
【新闻资讯】查看全部
亚洲双酚A价格创历史新高
2021-03-16 搜料网资讯: 受供应有限和需求旺盛等因素影响,近日,亚洲双酚A(BPA)价格飙升至历史高位。自去年11月以来,亚洲双酚A价格一直在上涨,目前价格已达吨2800-3000美元/吨。 据悉,韩国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |