牌号简介 About |
---|
Menzolit® HPC 1300是一种基于不饱和聚酯树脂的片状模塑料。该产品是玻璃纤维增强,含有矿物填料。如果发生火灾,产品不会熔化,也不会形成液滴,也不会产生过量的烟雾。这种材料是在加热的钢模中压缩成型的。建议使用镀铬工具。该产品不含卤素。Menzolit® HPC 1300是一种用于高强度应用的特殊SMC。玻璃料位的选择是为了在定向方向上结合塑性和高强度和刚度特性。增强材料由短切、随机分布的玻璃纤维和额外的无阻塞、连续和纵向取向的玻璃纤维组成。这导致单向纤维具有很高的刚度和强度特性。降低了定向流动性。这种取向影响成型过程中的流动,在零件设计和零件成型过程中必须牢记各向异性材料的特性。典型应用是承重部件,例如保险杠和动力传动系子结构。 Menzolit® HPC 1300 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® HPC 1300 is a special SMC for high strength applications. The glass level has been selected to combine mouldability with high strength and stiffness properties in orientation direction. The reinforcement is composed of chopped, randomly distributed glass fibers and additional unchopped, continuous and lengthwise oriented glass fibers. This leads to very high stiffness and strength properties along with the unidirectional fibers. The flowabilty in orientation direction is reduced. This orientation influences flow during moulding and the anisotropic material properties have to be kept in mind during part design and part moulding. Typical applications are load bearing components, for instance bumpers and power train substructures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.70 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
-- -- |
-0.030 | % | ISO 2577 |
-- -- 3 |
0.0 | % | DIN 53464 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
< 0.50 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
模压成型 Compression Molding |
25000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 14126 | |
泊松比 Poisson's ratio |
内部方法 | ||
Matrix Crazing Strain Matrix Crazing Strain |
% | 内部方法 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
模压成型 Compression Molding |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature |
℃ | 内部方法 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Post Molding Shrinkage |
【新闻资讯】查看全部
抚州市质监局官网通报产质量量市级监督抽查状况
2018-12-18 12月14日,抚州市市场和质量监督管理局官网通报2018年第2季度产品质量市级监督抽查情况,共抽查了抚州市 19家企业生产的20批次产品,经检验,16家企业生产的17批次产品质量合格,抽查合格率为85%;检出3批次产品质量不合格,不合格产品检出率为15%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |