| 牌号简介 About |
|---|
| PA 6用于注塑，用35%玻璃纤维化学增强，热稳定，耐170°C长时间热冲击。用于长时间温度高达200°C的环境中。在170°C下5000小时后，拉伸强度降低50%。应用：电热工具、爱好工具、齿轮、电器盖的手柄。热稳定预先决定了这些产品的环境与长期的热应力，如：进气管，气缸盖，感应线圈，携带零件在电机区域固定电机。以黑色交付。 PA 6 for injection moulding, chemically reinforced with 35% glass fibre, heat stabilized, mouldings resistant against long-time heat impact up to 170°C. Used in environment, where long-time temperatures up to 200°C occur. Decrease in tensile strength by 50% after 5000 hours at 170°C. Application: grips of electrotools, hobby tools, gears, covers of electric appliances. Heat stabilization predetermines these prodcts to an environment with longtime heat stress like eg.: intake piping, cylinder heads, induction coils, carrying parts in the motor fixing in the motor area. Delivered in black colour. |
产品描述 Product Description
用途：柔软的把手;电气/电子应用领域;动力/其它工具;齿轮;电器用具;
颜色：可用颜色,自然色,黑色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 化学耦合; 热稳定性好; Chemical coupling,Heat Stabilized,HB
填料：玻璃纤维 35
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.38 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
3.0 | g/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
STM 64 0808 | ||
|
TD TD |
0.80 | % | STM 64 0808 |
|
MD MD |
0.60 | % | STM 64 0808 |
|
含水量 water content |
0.15 | % | ISO 960 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
|
-20℃ -20℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
|
-20℃ -20℃ |
kJ/m² | ISO 179 | |
|
23℃ 23℃ |
kJ/m² | ISO 179 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | ISO 3146 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
|
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
|
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
塑化剂风波再起 平安成绩堪忧
2016-03-16 近日江苏省质监部门从实体店和电商平台上一共抽检了120批次塑料包书皮样品，其中包书套67批次，包书膜53批次。风险监测结果显示，有49批次不符合相关要求，占了样品总数的40.8%，不符合项目为溶剂残留、邻苯二甲酸酯(塑化剂)和多环芳烃。 3月3日，全国政协委员、中山大学食品与健康工程研究院院长刘昕表示，他将于今年两会期间提交《关于对可能降低人类生殖能力的环境激素污染物应引起高度关注的建议》的提案。他建议，首先应该做好环保塑化剂产业规划和项目引进，促进环保塑化剂产业链成长发展 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付