牌号简介 About |
---|
TECANYL® MT是为医疗器械应用开发的一个新的可高压消毒材料系列。该材料提供了理想的性能性能性能的PPSU为基础的树脂与加工容易和工具友好的缩醛或聚甲醛。这使得零件设计人员可以通过提高输出率和减少刀具磨损,在不牺牲零件性能的情况下,利用较低的制造成本。TECANYL® MT和TECANYL® MT xro形状都经过了ISO 10993测试,以支持其在仪器中的使用,仪器将与血液和组织接触不超过24小时。Ensinger还可提供TECANYL® MT级成品注塑成型零件,用于大批量应用。TECANYL® MT在需要暴露于极热和卫生措施的医疗器械中表现出广泛的优异性能。优良的磨损性能、易于加工的质量和广泛的颜色可用性有助于其在医疗器械中的应用。 TECANYL™ MT is a new family of autoclavable materials developed for medical device applications. The material offers the desired performance properties of PPSU based resins with the machining ease and tool friendliness of acetal or POM. This allows part designers to take advantage of lower manufacturing costs by increasing output rates, and reducing tool wear, all without sacrificing part performance. TECANYL™ MT and TECANYL™ MT XRO™ shapes are all ISO 10993 tested to support their use in instrumentation that is intended to come in contact with blood and tissue for a period of not more than 24 hours. Ensinger can also provide TECANYL™ MT grades in finished injection molded parts for high volume applications. TECANYL™ MT exhibits a broad range of outstanding properties for applications in medical devices where exposure to extreme heat and hygienic measures are demanded. Excellent wear properties, ease of quality machining and availability in a wide range of colors contribute to its desirability in medical devices. Excellent autoclave performance comparable to higher temperature materials Easily machined, producing high quality surface No black speck generation as in sulfone polymers Lower manufacturing costs ISO 10993 Tested |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.08 | g/cm³ | ASTM D792 |
-- -- |
0.830 | g/cm³ | ISO 1183 |
吸水率 Water absorption rate |
|||
平衡,23℃ Equilibrium, 23 ℃ |
0.23 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
3250 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
67.6 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:4~38℃ MD:4~38℃ |
1/℃ | ASTM E831 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
阿科玛和日本触媒强强联手生产LiFSI超纯电解质盐
2022-06-10 根据阿科玛的官方网站消息,日本触媒(Nippon Shokubai)和阿科玛(Arkema)正在联合进行可行性研究,并成立一家合资企业,将在法国建立一家工业工厂来生产LiFSI(二氟磺酸锂)超纯电 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |