BJ368Mo是一种流动性好、高刚度和高冲击强度的最佳组合的聚丙烯共聚物。采用硼化成核技术对材料进行了成核。流动特性、形核和良好的刚度使循环时间减少。该材料具有良好的抗静电性能和良好的脱模性能。 BJ368MO is a polypropylene copolymer characterized by good flow, and optimum combination of high stiffness and high impact strength. The material is nucleated with Borealis Nucleation Technology (BNT). Flow properties, nucleation and good stiffness give potential for cycle time reduction. The material have good antistatic performance and good mould release properties. Applications Thin wall containers Special Features stiffness and impact balance Good flow behaviour Reduced cycle time and increased output |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
70 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
1500 | MPa | ISO 527-2/50 |
拉伸强度 tensile strength |
|||
屈服 yield |
25.0 | MPa | ISO 527-2/50 |
拉伸应变 Tensile strain |
|||
屈服 yield |
4.0 | % | ISO 527-2/50 |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃ -20℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
℃ | ISO 75-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
巴斯夫全新的亚太区设计平台在上海成立
2016-06-01 巴斯夫在上海成立全新的亚太设计平台,旨在通过这一平台与亚太地区的设计师增强联系。 designfabrik®致力于帮助亚太地区的设计师实现他们的理念,通过结合创意和不同材料各种可能性,将理念转化为现实。除了 designfabrik,巴斯夫还将在这一平台上进行涂料解决方案、护理化学品、化学建材、颜料和皮革化学品领域的设计活动。作为亚太区设计活动的枢纽,它将为汽车、化妆品、建筑和消费品等行业提供先进的解决方案。 新设计平台坐落于巴斯夫亚太创新园(上海),这里不 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |