牌号简介 About |
---|
杜邦Fusabond® C190是一种酸酐改性的乙烯-醋酸乙烯酯共聚物。用途:胶管涂料聚合物改性剂 DuPont™ Fusabond® C190 is a anhydride modified ethylene vinyl acetate copolymer. Fusabond C190 is a grade with a higher level of anhydride modification, and is mainly intended for use as a component in a blend with other polyolefin resins. It is not intended for extrusion in its pure form in typical extrusions or coextrusions. Uses Adhesives Pipe Coating Polymer Modifier |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.950 | g/cm³ | ASTM D792 |
密度 Density |
0.950 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
16 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
16 | g/10min | ISO 1133 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature |
71.0 | ℃ | ASTM D3418 |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
加工温度 Processing temperature |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
模具对钢材有六大功能要求
2016-07-06 1、硬度 模具在工作时受力状态是复杂的,如热作模具通常是在交变的温度场下承受交变应力作用,因此它应具有良好的抗软化或塑性变形状态的能力,在长期工作环境下仍能保持模具的形状和尺寸精度。硬度是模具钢的重要性能之一。对冷作模具的硬度一般选择在58HRC以上,而热作模具尤其是要求高的抗热疲劳性能的模具,通常硬度在45HRC左右。对普通使用的塑料模具,一般硬度要求在35HRC左右。 2、强度与韧度 零件的成型使模具承受着巨大的冲击、扭曲等负荷,尤其是现 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |