| 牌号简介 About |
|---|
| 这一等级结合了非常高的抗冲击性，也在低温下，具有很高的刚度和良好的流动性能。SABIC® PP PHC26由于其分子量分布窄、翘曲倾向低、表面质量优良，因此通常用于行李箱壳体、板条箱和汽车零部件的注塑成型。本文所述产品尤其未经测试，因此未经验证可用于医药/医疗应用。 This grade combines very high impact resistance, also at low temperatures, with high stiffness and offers good flow properties. Due to its narrow molecular weight distribution, the very low tendency to warp and the excellent surface quality, SABIC® PP PHC26 is typically used in injection moulding of suitcase shells, crates & boxes and automotive parts. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
产品描述 Product Description
用途：皮箱;汽车领域的应用;装货箱;
加工条件：注射成型 Injection Molding
性能特点： 成核的; 嵌段共聚物; 机械强度好; 耐低温冲击; 窄分子量分布; 低翘曲性; 冲击性能好; 易流动; 表面光泽度好; Good Rigidity,Low warping,Good surface appearance,High impact resistance,Good liquidity,Nucleation,Block Copolymer,Weight distribution,low-temperature impact resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.905 | g/cm³ | ASTM D792 , ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
8.0 | g/10min | ASTM D1238，ISO 1133 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
|
-20℃ -20℃ |
9.0 | kJ/m² | ISO 179/1eA |
|
0℃ 0℃ |
15 | kJ/m² | ISO 179/1eA |
|
23℃ 23℃ |
60 | kJ/m² | ISO 179/1eA |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
23℃ 23℃ |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-20℃ -20℃ |
J/m | ASTM D256-A | |
|
0℃ 0℃ |
J/m | ASTM D256-A | |
|
23℃ 23℃ |
ASTM D256A , ISO 180/1A | ||
|
-20℃ -20℃ |
kJ/m² | ISO 180-1A | |
|
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
|
0.45 MPa，未退火 0.45 MPa, unannealed 4 |
℃ | ISO 75-2/Bf | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed 4 |
℃ | ISO 75-2/Af | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
-- -- |
℃ | ASTM D1525 5 , ISO 306/A120 5 | |
|
B120 B120 |
℃ | ASTM D1525 6 , ISO 306/B120 6 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D Shaw's D |
ISO 868 | ||
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
|||
|
1% 正割 1% secant 2 |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
屈服 yield |
MPa | ISO 527-2/1A/50 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield 3 |
% | ASTM D638 | |
|
屈服 yield |
% | ISO 527-2/1A/50 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 0.20 in/min |
| 3 2.0 in/min |
| 4 testbar 80*10*4mm |
| 5 标准 B (120°C/h), 压 力1 (10N) |
| 6 标准 B (120°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
国家能源局印发2022年能源工作指导意见
2022-03-29 近日，国家能源局印发《2022年能源工作指导意见》。 根据意见，全国能源生产总量达到44.1亿吨标准煤左右，原油产量2亿吨左右，天然气产量2140亿立方米左右。、，电力装机达到26亿千 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付