牌号简介 About |
---|
产品描述:SABIC® LDPE HP4024W是一种低密度聚乙烯级,采用防滑和防堵添加剂配制而成。它通常表现出良好的下拉能力和更高的输出。薄膜具有良好的光学性能、低摩擦和低阻塞性。典型应用:纺织包装薄膜,高清晰度洗衣袋,通用薄膜。本产品不适用于医疗和制药应用。 PRODUCT DESCRIPTION: SABIC® LDPE HP4024W is a Low Density Polyethylene grade formulated with slip and anti-block additives. It typically exhibits excellent draw down ability with higher output. Films typically exhibit good optics, low friction and low blocking. TYPICAL APPLICATIONS: Thin film for textile packaging, high clarity laundry bags, general purpose film. This product is not intended for use in medical and pharmaceutical applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
4.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
0.05 mm 0.05 mm |
260 | MPa | ISO 527-2 |
摩擦系数 friction coefficient |
< 20 | % | ISO 8295 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
薄膜厚度 film thickness |
|||
拉伸强度 tensile strength |
ISO 527-3 | ||
屈服,0.05 mm Yield, 0.05 mm |
MPa | ISO 527-2 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
20°,50 µm,吹塑薄膜 20 °, 50 µ m, blow molded film |
ASTM D2457 | ||
60°,50.0 µm,吹塑薄膜 60 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blow(up Ratio) Blow(up Ratio) |
备注 |
---|
1 Erucamide |
2 Natural Silica |
3 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
朗盛:以投资保证将来
2017-05-27 2017年5月26日,上海――特殊化学品公司朗盛的全资子公司赛拓有限公司将于欧洲精细化工展览会上展示其常规及定制合成服务。此次国际精细与特殊化工展将于2017年5月31日至6月1日在慕尼黑举办。赛拓专注于活跃化学原料与中间体的定制合成服务,并将利用此次展会展示其范围广泛的专业知识与技术,涉及行业包括农业、制药及精细化学品等。 赛拓目前正在全面执行其大型投资计划,确保其合成技术始终保持在世界一流水平,并且可充分满足客户项目的需求。该计划已投入约6000万欧元,用于翻新和扩建公 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |