牌号简介 About |
---|
UL412A采用Unipol工艺技术制造。UL412A具有良好的机械性能、光学性能和加工性能。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
40 | µm | |
抗张强度 Tensile strength |
|||
MD:断裂,40 µm,吹塑薄膜 MD: fracture, 40 µ m, blow molded film |
40.2 | MPa | |
TD:断裂,40 µm,吹塑薄膜 TD: fracture, 40 µ m, blow molded film |
36.3 | MPa | |
拉伸应变 Tensile strain |
|||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
g | ||
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
g | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40 µm,吹塑薄膜 45 °, 40 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40.0 µm,吹塑薄膜 40.0 µ m, blow molded film |
% | ASTM D1003 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
朗盛推出新型浇注型聚氨酯弹性体预聚体
2018-04-26 特种化学品公司朗盛开发了用于热浇铸弹性体的新型聚酯型预聚物Vibrathane 7085。它拥有MDI端基(二苯甲烷二异氰酸酯)可用1,4-丁二醇固化成浇注型聚氨酯弹性体,其特点是在83至87邵氏A硬度下具有低压缩形变和抗高撕裂强度的特点。朗盛聚氨酯系统业务部全球研发与创新中心的专家Nitin Sharma博士表示“这是材料的特性,两种性能呈反向影响,所以通常不能同时优化”。通用型预聚物可在催化作用下以更低成本生产,以满足更广泛的的弹性体需求。 Sharma补充表示:“相关应用包括模切毛毯 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |