| 牌号简介 About |
|---|
| LLC6-020是一种乙烯-己烯共聚物认证的基本树脂，适用于要求高强度、韧性、高清晰度、低刚度和良好拉伸性能的薄膜的平模铸造挤出。LLC6-020不含防滑块。LLC6-020符合FDA第21CFR 177.1520（c）3.1a号法规以及大多数与食品接触的聚乙烯使用相关的国际法规。可用添加剂B=赤脚A=0打滑/高防阻块F=全添加剂 LLC6-020 is an Ethylene-Hexene copolymer certified prime resin for CAST Flat-Die extrusion of film applications requiring high strength, toughness, excellent clarity, low stiffness, and good tensile properties. LLC6-020 contains no slip and no antiblock. LLC6-020 complies with FDA regulation 21CFR 177.1520(c) 3.1a, and with most international regulations concerning the use of Polyethylene in contact with food articles. AVAILABLE ADDITIVES B = Barefoot A = 0 Slip/ High Antiblock F = Full Additives |
产品描述 Product Description
用途：流延薄膜;
加工条件：流延薄膜
性能特点： 机械强度好; 共聚物; 透光性好; 己烯共聚单体; 食品接触; 低密度; 韧性好; Good Rigidity,Good Clarity,Good flexibility,Food contact compliance,Low density,Copolymer,Hexene copolymers
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
2.0 | g/10min | ASTM D1238 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
20 | µm | |
|
割线模量 Secant modulus |
ASTM D882 | ||
|
1% 正割，MD：20 µm 1% secant, MD: 20 µ m |
150 | MPa | ASTM D882 |
|
1% 正割，TD：20 µm 1% secant, TD: 20 µ m |
170 | MPa | ASTM D882 |
|
拉伸强度 tensile strength |
ASTM D882 | ||
|
MD，屈服，20 µm MD, yield, 20 µ m |
MPa | ASTM D882 | |
|
TD，屈服，20 µm TD, yield, 20 µ m |
MPa | ASTM D882 | |
|
MD，断裂，20 µm MD, fracture, 20 µ m |
MPa | ASTM D882 | |
|
TD，断裂，20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
|
拉伸应变 Tensile strain |
ASTM D882 | ||
|
MD，断裂，20 µm MD, fracture, 20 µ m |
% | ASTM D882 | |
|
TD，断裂，20 µm TD, fracture, 20 µ m |
% | ASTM D882 | |
|
落锤冲击 Drop hammer impact 2 |
|||
|
20 µm 20 µm 2 |
g | ASTM D1709-A | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
|
MD：20 µm MD：20 µm |
g | ASTM D1922 | |
|
TD：20 µm TD：20 µm |
g | ASTM D1922 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，20.3 µm，吹塑薄膜 45 °, 20.3 µ m, blow molded film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
20.3 µm，吹塑薄膜 20.3 µ m, blow molded film |
% | ASTM D1003 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 F50 |
|
【新闻资讯】查看全部 
明白拉丝模具修补的进程
2016-08-22 模具修补技术无疑强化拉丝模具的寿命,经济效益好,可以应用各种铁基合金等各种金属材料模具及工件的表面强化及修复并大幅提高使用寿命。明确拉丝模具修补的具体过程很重要。 1、清理:在需要修补处作简单清理去除油污 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付