| 牌号简介 About |
|---|
| Amodel AS- 4145 HS聚邻苯二甲酰胺（PPA）是热水可成型45％玻纤增强树脂。主要性能包括高耐热性，在宽的温度范围内具有高强度和刚度、低吸湿性、优异的耐化学性和优良的电性能。 该树脂是汽车电气和电子产品，包括连接器、插座、开关和传感器的理想选择。同时也是发动机罩下保护关键控制系统，如防抱死制动系统、牵引力控制系统、转向系统、发动机电子控制、传动和底盘控制单元等外壳材料的不错选择。快速结晶率和高流动性可以缩短生产周期，从而提高成型效率，降低成本。 -黑色：AS-4145 HS BK 324 Amodel® AS-4145 HS polyphthalamide (PPA) is a a 45% glass reinforced resin that is hot-water moldable. Key properties include high heat resistance, high strength and stiffness over a broad temperature range, low moisture absorption, excellent chemical resistance and excellent electrical properties. This resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Its rapid crystallization rate and high flow can result in shorter cycles, thereby enhancing molding productivity and lowering costs. Black: AS-4145 HS BK 324 |
产品描述 Product Description
用途：机器/机械部件;连接器;研磨清洁材料;金属取代;外壳;阀门/阀门部件;草坪和园林设备;汽车领域的应用;厚壁配件（部件）;工业应用;通用;工业部件;汽车电子;汽车的发动机罩下的零件;
颜色：黑色
加工条件：水温模具注塑成型
性能特点： 防火阻燃等级HB; 低吸湿性; 热稳定性好; 机械强度好; 尺寸稳定性好; 成型周期快; 耐化学性; 耐高温; 润滑性; 韧性好; Good Rigidity,Good flexibility,Good Dimensional Stability,Quick molding cycle,High Heat Resistance,Lubricating,Solvent resistance,Low moisture absorption,Heat Stabilized,HB
填料：玻璃纤维 45
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.55 | g/cm³ | ISO 1183/A |
|
收缩率 Shrinkage rate |
|||
|
TD TD |
1.0 | % | ASTM D955 |
|
MD MD |
0.50 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.21 | % | ASTM D570 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
15200 | MPa | ASTM D638 |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ISO 527-2 | |
|
断裂 fracture |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2 | |
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
屈服 yield |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
MPa | ASTM D732 | |
|
泊松比 Poisson's ratio |
ASTM E132 | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火，3.18 mm 1.8 MPa, annealed, 3.18 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
0.45 MPa，退火，3.2 mm 0.45 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
|
连续使用温度 Continuous use temperature 2 |
℃ | ASTM D3045 | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
熔融温度 Melting temperature |
℃ | ASTM D570 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD TD |
ASTM E831 | ||
|
0 到 90℃ 0 to 90 ℃ |
cm/cm/℃ | ASTM E831 | |
|
149 到 249℃ 149 to 249 ℃ |
cm/cm/℃ | ASTM E831 | |
|
MD MD |
ASTM E831 | ||
|
0 到 90℃ 0 to 90 ℃ |
cm/cm/℃ | ASTM E831 | |
|
149 到 249℃ 149 to 249 ℃ |
cm/cm/℃ | ASTM E831 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
|||
|
1.59 mm 1.59 mm |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
1 MHz 1 MHz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
|
高电压电弧起痕速率 High voltage arc marking rate |
|||
|
HVTR HVTR |
mm/min | UL 746 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level 3 |
|||
|
3.20 mm 3.20 mm |
UL 94 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 1200小时 |
| 3 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
|
【新闻资讯】查看全部 
宁夏约谈能耗双控形势严峻的地区和重点企业
2021-08-24 搜料网资讯： 22日上午，宁夏节能和化解过剩产能工作办公室对今年以来能耗双控目标完成情况一级预警的宁东能源化工基地、石嘴山市、中卫市、吴忠市4个地区发展改革、工信部门主 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付