牌号简介 About |
---|
Lotr_ne q2018 c是在气相反应器中生产的乙烯-丁烯共聚物。它的设计是为了在大多数电影应用中提供有竞争力的性能。在为LLDPE设计的流延膜机上,LOTR_NE Q1808C可以以较高的输出速率进行加工,挤压压力适中,气泡稳定性好,压力表控制好。Lotr_ne q2018 c可与吹塑薄膜单挤出或共挤中使用的LDPE或其他PE树脂有利地混合,以改善薄膜性能。lotr_ne q2018 c适用于消费者、工业、食品或卫生包装以及拉伸膜和农业膜等非包装应用,如覆盖膜。 Lotrène ® Q2018 C is an ethylene-butene copolymer produced in a gas phase reactor. It is designed for delivering competitive performance in most cast film applications. Lotrène ® Q2018 C can be processed at high output rates with moderate extrusion pressure, good bubble stability and gauge control on cast film machine designed for LLDPE. Lotrène ® Q2018 C can advantageously be blended with LDPE or other PE resins used in blown film mono extrusion or coextrusion to improve film properties. Lotrène ® Q2018 C is suited for many applications in the field of consumer, industrial, food or hygiene packaging as well as stretch film and non-packaging applications like agricultural films e.g. mulching films. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
拉伸模量 Tensile modulus |
ISO 178 | ||
1% 正割,MD,20 µm,铸造薄膜 1% secant, MD, 20 µ m, cast thin film |
165 | MPa | ISO 178 |
1% 正割,TD,20 µm,铸造薄膜 1% secant, TD, 20 µ m, cast thin film |
170 | MPa | ISO 178 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,20 µm,吹塑薄膜 MD, yield, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,20 µm,吹塑薄膜 TD, yield, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,20 µm,吹塑薄膜 MD, fracture, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,20 µm,吹塑薄膜 TD, fracture, 20 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,20 µm,挤塑薄膜 MD, fracture, 20 µ m, extruded film |
% | ISO 527-3 | |
TD,断裂,20 µm,挤塑薄膜 TD, fracture, 20 µ m, extruded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact 2 |
|||
20 µm,铸造薄膜 20 µ m, cast thin film 2 |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:20 µm,铸造薄膜 MD: 20 µ m, cast thin film |
N | ISO 6383-2 | |
TD:20 µm,铸造薄膜 TD: 20 µ m, cast thin film |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm,铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 标准 B (120°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
聚苯硫醚注塑成型稀有的3种缺陷,如何有的放矢?
2018-05-28 聚苯硫醚,全称为聚次苯基硫醚,英文名称polyphenyleneSulfide(简称PPS),是分子主链上带有苯硫基的热塑性工程塑料。 聚苯硫醚耐热性优良,长期使用温度在200℃;耐化学药品性好,具有近似 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |