牌号简介 About |
---|
高弹性和良好的弹性恢复良好的聚丙烯和聚乙烯软接触混合物的冲击强度符合欧盟,10/2011号符合美国FDA 21 CFR 175.105 DFDB-1085 NT非常低密度聚乙烯(VLDPE)树脂是通过道氏气相聚合生产的。这是一种乙烯-丁烯共聚物,具有很高的柔韧性和弹性。它可用于单层和共挤薄膜以及与其他聚烯烃的混合物中,以增强结构的韧性。 High elasticity with good elastic recovery Excellent impact strength in blends with polypropylene and polyethylene Soft touch blend Complies with EU, No 10/2011 Complies with U.S. FDA 21 CFR 175.105 DFDB-1085 NT Very Low Density Polyethylene (VLDPE) Resin is produced via gas phase polymerization from Dow. This is an ethylene-butene copolymer exhibiting high flexibility and elasticity. It can be utilized in monolayer and coextruded films and in blends with other polyolefins to enhance toughness of the structure. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.884 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.75 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
26 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
-52.2 | ℃ | 内部方法 |
熔融温度 Melting temperature |
|||
DSC DSC |
114 | ℃ | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,1 秒 Shore A, 1 second |
ASTM D2240 | ||
邵氏 A,5 秒 Shore A, 5 seconds |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
2% 正割 2% secant |
MPa | ASTM D790-A |