| 牌号简介 About |
|---|
| Noryl 731F树脂PPE+PS混合物。未填充的NSF列出了几种颜色的饮用水（标准61）。符合FDA的多种颜色（限制适用）。UL94 HB额定值。吸水率低。水解稳定性。尺寸稳定性。适用于流体工程应用：阀门组件、水泵外壳等。该等级将不再支持生物相容性信息，不应用于需要生物相容性的医疗应用。替代级HN731A.Noryl 731F树脂PPE+PS，HDT 125 PPE+PS blend. Unfilled. NSF listed for potable water use in several colors (Standard 61). FDA compliant in several colors (restrictions apply). UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications: valve components, water pump housings, etc. This grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HN731A. |
产品描述 Product Description
用途：阀门/阀门部件;泵件;饮用水应用;外壳;
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级HB; 尺寸稳定性好; 吸水率低; 耐水解; Good Dimensional Stability,Hydrolysis stability,Low or no water absorption,HB
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.06 | g/cm³ | ASTM D792 |
|
密度 Density |
1.06 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
280℃，5.0kg 280℃，5.0kg |
9.2 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
280℃，5 kg 280℃，5 kg |
9.00 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
TD：3.2 mm TD：3.2 mm |
0.50 to 0.70 | % | 内部方法 |
|
MD：3.2 mm MD：3.2 mm |
% | 内部方法 | |
|
吸水率 Water absorption rate |
|||
|
饱和，23℃ Saturation, 23 ℃ |
% | ISO 62 | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
|
24hr 24hr |
% | ASTM D570 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength 8 |
|||
|
23℃ 23℃ 8 |
kJ/m² | ISO 179/1eA | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-40℃ -40℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 9 |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
|
23℃，Total Energy 23℃，Total Energy |
J | ASTM D3763 | |
|
落锤冲击 Drop hammer impact |
ASTM D3029 | ||
|
-40℃ -40℃ |
J | ASTM D3029 | |
|
-30℃ -30℃ |
J | ASTM D3029 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
1.8 MPa，未退火，64 mm跨距 1.8 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Af | |
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 11 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ISO 11359-2 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ISO 11359-2 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电强度 Dielectric strength |
|||
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
耐电弧性 Arc resistance 12 |
ASTM D495 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
高电压电弧起痕速率 High voltage arc marking rate |
|||
|
HVTR HVTR |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength 3 |
|||
|
断裂 fracture 3 |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2/50 | |
|
屈服 yield |
MPa | ISO 527-2/50 | |
|
屈服 yield 3 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 3 |
|||
|
断裂 fracture 4 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/50 | |
|
屈服 yield |
% | ISO 527-2/50 | |
|
屈服 yield 3 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
ASTM D790 | ||
|
100 mm跨距 100 mm span 4 |
MPa | ASTM D790 | |
|
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus 6 |
MPa | ISO 178 | |
|
弯曲强度 bending strength 6 , 7 |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
ASTM D790 | ||
|
屈服，50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
|
屈服，100 mm跨度 Yield, 100 mm span 4 |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 50% RH |
| 3 0.20 in/min |
| 4 2.0 in/min |
| 5 类型 1, 2.0 in/min |
| 6 0.051 in/min |
| 7 0.10 in/min |
| 8 0.079 in/min |
| 9 Yield |
| 10 80*10*4 sp=62mm |
| 11 80*10*4 |
| 12 80*10*4 mm |
| 13 标准 B (120°C/h), 载荷2 (50N) |
| 14 钨电极 |
|
【新闻资讯】查看全部 
高盟新材拟收购新蓝天新材料51%股权
2020-12-26 搜料网资讯： 12月21日晚间，高盟新材发布公告称，公司正在筹划发行股份及支付现金购买资产事项，可能会构成《上市公司重大资产重组管理办法》规定的重大资产重组情形，因有关事 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付