| 牌号简介 About |
|---|
| Clearflex CLH D0是一种线性低密度聚乙烯，含抗氧化剂，以极低密度（VLDPE）为特征。这种树脂是用专有技术生产的。用CLH-D0生产的拉伸膜具有高拉伸性、高清晰度和很高的粘着力。主要应用ClearFlex CLHD0推荐用于所有需要卓越灵活性和韧性的应用。其独特的大分子结构，由于采用了“独特”的专有催化剂，使Clearflex CLHD0成为电线电缆复合的理想选择，由于其优良的聚烯烃相容性和填料可接受性，Clearflex CLHD0被推荐为PP的冲击改性剂，有或无矿物填料。 Clearflex CLH D0 is a linear low density polyethylene, with antioxidants, characterised by a very low density (VLDPE). This resin is produced with a proprietary technology. Stretch films manufactured with Clearflex CLH D0 have high stretchability, outstanding clarity and very high constancy in cling effect. Main Applications Clearflex CLHD0 is recommended in all applications where outstanding flexibility and toughness are required. Its peculiar macromolecular structure, as a result of a "unique" proprietary catalyst employed, makes Clearflex CLHD0 the ideal choice for wire and cable compounding and, due to its excellent polyolefin compatibility and fillers acceptance, Clearflex CLHD0 is recommended as impact modifier of PP, with or without mineral fillers. |
产品描述 Product Description
用途：薄膜;流延薄膜;
加工条件：流延薄膜
性能特点： 抗氧化; 透光性好; 食品接触; Good Clarity,Food contact compliance,Inoxidizability
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.900 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
3.0 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
摩擦系数 friction coefficient |
|||
|
动态，铸造薄膜 Dynamic, cast thin film |
> 0.50 | ISO 8295 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
23 | µm | |
|
薄膜厚度 film thickness |
8 to 50 µm | ||
|
拉伸模量 Tensile modulus |
ISO 527-3 | ||
|
1% 正割，MD，23 µm，铸造薄膜 1% secant, MD, 23 µ m, cast thin film |
MPa | ISO 527-3 | |
|
1% 正割，TD，23 µm，铸造薄膜 1% secant, TD, 23 µ m, cast thin film |
MPa | ISO 527-3 | |
|
拉伸强度 tensile strength |
ISO 527-3 | ||
|
MD，屈服，23 µm，吹塑薄膜 MD, yield, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，屈服，23 µm，吹塑薄膜 TD, yield, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
|
MD，断裂，23 µm，吹塑薄膜 MD, fracture, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
|
TD，断裂，23 µm，吹塑薄膜 TD, fracture, 23 µ m, blow molded film |
MPa | ISO 527-3 | |
|
拉伸应变 Tensile strain |
ISO 527-3 | ||
|
MD，断裂，23 µm，铸造薄膜 MD, fracture, 23 µ m, cast thin film |
% | ISO 527-3 | |
|
TD，断裂，23 µm，铸造薄膜 TD, fracture, 23 µ m, cast thin film |
% | ISO 527-3 | |
|
落锤冲击 Drop hammer impact |
|||
|
23 µm，铸造薄膜 23 µ m, cast thin film |
g | ISO 7765-1/A | |
|
撕裂强度 tear strength 2 |
ISO 6383-2 | ||
|
MD，23 µm MD，23 µm |
kN/m | ISO 6383-2 | |
|
TD，23 µm TD，23 µm |
kN/m | ISO 6383-2 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
℃ | 内部方法 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，23 µm，铸造薄膜 45 °, 23 µ m, cast thin film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
23 µm，铸造薄膜 23 µ m, cast thin film |
% | ISO 14782 | |
| 备注 |
|---|
| 2 Cast Film |
|
【新闻资讯】查看全部
模具吹塑成型几大优势
2016-08-26 (1)熔体被注入型坯模具型腔内时在周向受到一定的取向效应。此外,型坯吹胀时的温度比挤出吹塑的低些,吹胀产生的取向效应能较多地保留下来,这些有助于提高容器的强度等性能。 (2)容器尺寸(尤其是颈部螺纹尺寸)精度高:较易于按要求保证容器壁厚的均匀性,容器规格均一。 (3)容器上不形成接合缝,不需修整,一般不产生边角料(挤出吹塑产生的边角料通常为5%~30%)。 (4)吹塑模具上可设置滑动式底模块,故容器底部形状的设计灵活性较大。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |