| 牌号简介 About |
|---|
| EPALEX 7517 UV3 SAS是一种热塑性橡胶改性矿物填充聚丙烯化合物。这是一个非常高的流动注射成型等级开发的零件长流动长度和高冲击强度在零下温度，同时保持良好的刚性在高环境温度。该材料显示出最小的收缩率和较低的CLTE。它含有抗静电剂和脱模剂，可在室外持续风化。 Epalex 7517 UV3 SAS is a thermoplastic rubber modified mineral filled polypropylene compound. It is a very high flow injection moulding grade developed for parts with long flow lengths and high impact strength at sub-zero temperatures whilst maintaining good rigidity at high ambient temperatures. The material displays minimal shrinkage and low CLTE. It contains an antistatic agent and mould release and is stabilized for continuous outdoor weathering. |
产品描述 Product Description
用途：汽车防撞杆;汽车领域的应用;
加工条件：注射成型 Injection Molding
性能特点： 抗静电; 机械强度好; 耐低温冲击; 流动性高; 热膨胀系数低; 冲击性能好; 收缩性低; 耐候抗UV; Good Rigidity,Weather resistance is good,Low CLTE,High impact resistance,High liquidity,Low contractility,Antistatic property,low-temperature impact resistance
紫外线：UV Stabilized
填料：矿物
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.08 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
19 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.0 mm MD：3.0 mm |
0.50 到 0.90 | % | ASTM D955 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
-20℃，3mm -20℃，3mm |
240 | J/m | ASTM D256 |
|
0℃，3mm 0℃，3mm |
410 | J/m | ASTM D256 |
|
23℃，3mm 23℃，3mm |
J/m | ASTM D256 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火，3.0 mm 0.45 MPa, unannealed, 3.0 mm |
℃ | ASTM D648 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-30~30℃，3.00 mm MD：-30~30℃，3.00 mm |
1/℃ | ASTM D696 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ASTM D2240 | ||
|
邵氏 D，3.00 mm Shore D, 3.00 mm |
ASTM D2240 | ||
|
邵氏 D，15 秒，3.00 mm Shore D, 15 seconds, 3.00 mm |
ASTM D2240 | ||
|
洛氏硬度 Rockwell hardness |
|||
|
R 级，3.00 mm R-grade, 3.00 mm |
ASTM D785 | ||
|
拉伸强度 tensile strength 2 |
|||
|
3 mm 3 mm 2 |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain 2 |
|||
|
断裂，3 mm Fracture, 3 mm 2 |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
3 mm 3 mm |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 2.0 in/min |
|
【新闻资讯】查看全部
2018年1-5月塑料制品业主营业务支出2541.54亿元
2018-07-23 2018年1-5月，全国塑料制品业主营业务收入2541.54亿元，同比增长7.26%;其中：塑料薄膜制造主营业务收入326.55亿元，同比增长5.36%;塑料板、管、型材的制造主营业务收入561.85亿元，同比增长14.56%;塑料丝、绳及编织品的制造主营业务收入149.7亿元，同比增长2.2%;日用塑料制品制造主营业务收入189.46亿元，同比下降4.65%。 来 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |