LNP Lubricomp Rel22是一种基于尼龙66树脂的化合物,含有10%的碳纤维和10%的聚四氟乙烯。这种材料的附加特性包括:耐磨、导电。又名:lnp*lubricomp*化合物RCL-4022产品再订购名称:rel22 LNP LUBRICOMP REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD:24 hrs MD:24 hrs |
0.30 到 0.50 | % | |
TD:24 hrs TD:24 hrs |
1.0 到 3.0 | % | |
吸水率 Water absorption rate |
|||
24hr,50% RH 24hr,50% RH |
0.81 | % | ASTM D570 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
1.2 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 2 |
MPa | ASTM D638 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
-- -- 6 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ISO 178 | |
断裂,50 mm跨度 Fracture, 50 mm span 7 |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
ASTM D3702 Modified | ||
与自身 - 动态 With oneself - dynamic |
|||
与自身 - 静态 With oneself - static |
|||
磨损因数 Wear factor |
ASTM D3702 Modified | ||
Ring Ring |
10^-10 in^5-min/ft-lb-hr | ||
Washer Washer |
10^-10 in^5-min/ft-lb-hr | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 8 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 9 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
-- -- |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 10 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 11 |
℃ | ISO 75-2/Af | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM D696 | ||
MD:-30~30℃ MD:-30~30℃ |
1/℃ | ||
TD:-30~30℃ TD:-30~30℃ |
1/℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0,20 in/min |
3 类型 1, 0,20 in/min |
4 0,051 in/min |
5 0,079 in/min |
6 80*10*4 |
7 80*10*4 mm |
【新闻资讯】查看全部
日本信越化学公司正在加紧研发高回弹性TPU资料
2018-06-19 日本信越化学公司正在加紧研发高回弹性TPU材料。在汽车应用领域,公司开发出了针对汽车零部件的TPU 注塑等级,使得TPU 材料可以用作汽车零部件的生产,由于该公司研发的TPU材料具有无粘性及回弹性好的特点,因而在运动用品及玩具领域已经得到了广泛应用。公司正在着手生产TPU材质的汽车部件,以满足新能源汽车轻量化的需求。 此外,由于TPU材料有着极高的阻燃性,在各种工业用途中也逐步扮演着越来越重要的角色。公司也将持续加大投入,不断开拓TPU 材料用途。 TPU名 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |