牌号简介 About |
---|
产品描述:Eastman Treva是一种新型的纤维素基工程生物塑料,具有高性能和低环境影响。Treva耐化学腐蚀,尺寸稳定,流动性好,不含双酚A,双折射率低。美国农业部(USDA)生物参考计划已认证Eastman Treva工程生物塑料GC6021,生物基础含量为42%。关键特性:无BPA尺寸稳定性优异耐化学性优异流动性低双折射应用/用途:复杂复杂零件化妆品电子产品和外壳可穿戴设备和耳机 Product Description: Eastman TREVA™ is a new cellulose-based engineering bioplastic that offers both high performance and reduced environmental impact. TREVA is chemically resistant, dimensionally stable and has excellent flow, BPA-free and low birefringence. The United States Department of Agriculture's (USDA's) BioPreferred® program has Certified Eastman TREVA™ Engineering Bioplastic GC6021 with a biobased content of 42%. Key Attributes: BPA-free Dimensional stability Excellent chemical resistance Excellent flow Low birefringence Application/Uses: Complex and intricate parts Cosmetics Electronics and housings Wearable devices and headphones |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.80 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
2.2 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃ -40℃ |
80 | J/m | |
23℃ 23℃ |
200 | J/m | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 3 |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
维卡软化温度 Vicat Softening Temp 3 |
℃ | ASTM D1525 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Renewable Content Renewable Content |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ||
断裂 fracture |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
3. Conditioned 4 hours at 70°C (158°F). |
【新闻资讯】查看全部
OLED照明器件薄膜封装零碎研制开发成功
2016-02-16 近日,大尺寸OLED照明器件薄膜封装系统研制开发成功。该系统可在真空条件下连续完成器件制备和封装。日前,该项目通过了中科院条件保障与财务局的专家现场验收。 OLED照明器件薄膜封装系 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |